Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX9400W - Asia - (PPE+PA*) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL GTX™ Resin GTX9400W - Asia:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Noryl GTX datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
NORYL GTX™ 9400W resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA) that exhibits high heat resistance, high flow, and added mold release. NORYL GTX9400W resin is injection moldable and an excellent candidate for automotive under-the-hood applications such as power distribution boxes, relay boxes, connectors, sensors, and fuse box covers.

UL Yellow Card Link E207780-615350
Processing/Physical Characteristics値単位テスト基準
ASTM数据
メルトフローレイト, MFI 97 g/10min ASTM D 1238
温度 280 °C -
荷重 5 kg -
機械的特性値単位テスト基準
ISO データ
降伏応力 69 MPa ISO 527
破壊ひずみ 39 % ISO 527
曲げ弾性率 2700 MPa ISO 178
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm 21 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 1950 MPa ASTM D 638
降伏応力 64 MPa ASTM D 638
破壊応力 62 MPa ASTM D 638
降伏点伸び 11 % ASTM D 638
破断伸び 40 % ASTM D 638
ノッチ付きIzod衝撃強さ, 1/8 in 256 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 112 J/m ASTM D 256
温度 -30 °C -
アイゾット衝撃試験, 1/8 in 849 J/m ASTM D 256
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 78 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 187 °C ISO 75-1/-2
ビカット軟化温度, B 203 °C ISO 306
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.5 mm -
ASTM数据
DTUL @ 66 psi 190 °C ASTM D 648
DTUL @ 264 psi 83 °C ASTM D 648
ビカット軟化温度 212 °C ASTM D 1525
その他の特性.値単位テスト基準
密度 1100 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 95 - 105 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.07 % -
樹脂温度 270 - 295 °C -
金型温度 65 - 95 °C -
Zone 1 255 - 295 °C -
Zone 2 260 - 295 °C -
Zone 3 265 - 295 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 1.4 MPa -
特殊な特性
成形加工法.
射出成形.
アプリケーション
自動車
領域別の利用可能性
アジア/太平洋地域.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com